Corrosion Preventive Compound
Product Description: 

RXSOL ANTI CORROSIVE AGENT  is a solvent cutback, wax base, general purpose, corrosion preventive compound.RXSOL ANTI CORROSIVE AGENT is excellent for long term protection of metallic surfaces against corrosion in either indoor or outdoor exposure and during domestic and international shipments, like machinery, machine rolls/tools, automatic parts, dies, tubing, and spare parts.RXSOL ANTI CORROSIVE AGENT cures to a dark amber colored, waxy, transparent, firm film.

Product Application: 

RXSOL ANTI CORROSIVE AGENT is formulated to be used as supplied. Ensure uniform consistency prior to use. Continued stirring is generally not required. If the product thickens due to cold storage or loss of solvent during use, contact Valvoline. DO NOT THIN RXSOL ANTI CORROSIVE AGENT. Incorrect thinning will affect film build, dry time and product performance.Rx Marine International recommends that the ambient and product temperature be 10-35 °C at the time of product application.RXSOL ANTI CORROSIVE AGENT can be applied by airless spray or brush.

Product Procedure: 

Net Materials by spray machine or Brush.

Product Note: 

Removal:
RXSOL ANTI CORROSIVE AGENT can be removed with mineral spirits or any similar petroleum solvent, hot alkaline wash or low pressure steam.

Storage:
RXSOL ANTI CORROSIVE AGENT should be stored at temperatures between 10-35 °C. Mild agitation is recommended prior to use. Due to its composition RXSOL ANTI CORROSIVE AGENT can be subject to postproduction viscosity changes during storage.Under proper storage conditions RXSOL ANTI CORROSIVE AGENT can have a shelf life of 4 years minimum.

Caution:
Adequate ventilation is required for cure and to ensure against formation of combustible liquid. THE PARTIALLY CURED FILM SHOULD NOT BE EXPOSED TO IGNITION SOURCES SUCH AS FLARES, FLAMES, SPARKS, EXCESSIVE HEAT OR TORCHES. Refer to  Material Safety Data Sheet for additional handling and first aid information.
  
Note:
The addition of any product over or under this coating is not recommended. The use of additional coatings could result in chemical incompatibility, thus affecting the performance of this coating as stated in the Typical Properties section.

Product Technical Specification: 

Typical Properties

Flashpoint; PMCC 40  °C
Specific Gravity @ 60°F 0.87 kg/ltr
Recommended Dry Film Thickness  50  microns minimum
Theoretical Coverage @ Avg. Recommended DFT 9.2 m²/l
Non Volatile 52 weight %

Viscosity; DIN (53 211) Cup No. 4 @ 20°C

(at time of manufacture)

85 seconds

 

Dry to Touch Time @ 25°C  ± 2  hours
Cure Time @ 25°C ± 24  hours
 
Volatile Organic Content (VOC) (ASTM D-3960) 415  g/l

Accelerated Corrosion Tests:
@ Avg. Recommended DFT
 

Salt Spray; 5 % NaCl @ 35°C; DIN 50 021 (ASTM B-117) (DIN 1623 Steel Panels) 40+  days
 
Humidity; 100 % RH; @ 40°C; DIN 50 017-KK (DIN 1623 Steel Panels) 100+ days
 
Product pack size: 
RXSOL ANTI CORROSIVE AGENT is available in 5 Ltr, 25 Ltrs, and 210 Ltrs.
Product alias: 
<p> Ferro Guard 100E, Tectyl 506, nox rust 366, REMIDOL 1541- ANTICORROSIVE</p>
Articles: 
Remarks: 

Anti Corrosive Agent manufacturer, exporter and supplier in Baraka - Oman, Fujairah, Dubai, Sharjah, Abudhabi, Ajman, Mumbai, Kandla, Kolkata, Visakhapatnam, Chennai, Muscat Barka Oman, Sohar, Yemen, Sudan, Nairobi Kenya Africa


Product Delivery Locations: 
Kattupalli Port ( L & T Shipbuilding Limited shipyard ), Ennore Port ( Coromondel International Limited Port Area ), Chennai Port, Mugaiyur port, Thiruchopuram port, Silambimangalam Shipyard, Parangipettai port, PY-03 Oil Field, Kaveri port, Vanagiri port, Thirukkadaiyur port, Thirukkuvalai port, Punnakkayal port, Udangudi port, Manappad port, Koodankulam port, Chettinad Tharangambadi Port, Mathur SIDCO Industrial area, Sipcot Industrial Park Malayambakkam

Product Articles